Automotive components powder coatings MT-A1230/MT-EN155G /MT-PE 55-9403

MOQ;	MOQ100KG，From China
Feature	Powder Coating & Surface Finishing Solutions
Classification	Powder Coating
Advantage	Professional, Fast Delivery, Customizable
Samples	Apply for free，Contact us now.

EMAIL
services@moutainchem.com

Surface Finish Options Overview

Product Description

MT-A1230 series covers a wide range of powder coatings specifically designed to meet the extreme demands of automotive components. Demanding environments require high performance protection. MT-A1230 will enhance and protect automotive parts with excellent chemical, corrosion and chip resistance as well as the right aesthetic appearance exactly where it’s needed.

Powder properties

Chemical Type	Epoxy-Polyester
Area of usage	Automotive mechatronic components and systems
Related Specifications	Brose 587000-110 / Group 2
Appearance	Smooth
Gloss level (60°)	52 ± 4 GU
Colour	Black
Recommended Film Thickness (µm)	80 ± 40 µm
Density (g/cm3)	1.46 ± 0.03
Gel time (at 200 °C)	36 – 54sec
Coverage at 60 µ Coverage at 80 µ	93.0 g/m2 or 10.8 m2/kg 124.0 g/m2 or 8.1 m2/kg
Application	Corona Only – Electrostatic (30 – 100 kV)
Storage	Under dry, cool (<25°C) conditions
Shelf life	At least 12 months from production date
Curing schedule (at object temperature)	10 minutes at 180°C (please see curing window)

Mechanical Tests

Adhesion	DIN EN ISO 2409	Gt 0
Erichsen cupping	DIN EN ISO 1520	≥ 5 mm
Buchholz indentation	DIN EN ISO 2815	> 80
Cylindrical mandrel	DIN EN ISO 1519	≤ 6 mm

Application

MT-A1230 powders can be applied by manual or automatic electrostatic spray equipment. It is recommended that for consistent application and appearance product be fluidized during application. Unused powder can be reclaimed using suitable equipment and recycled through the coating system.

Pre-treatment

Steel surfaces to be coated must be clean and free from grease. For maximum protection it is essential to pre-treat components prior to the application of MT-A1230. Iron Phosphate and Zinc Phosphate of ferrous metals improve corrosion resistance.